Fracture Mechanism of Flexible Insulation at High Temperature
DOI:
Author:
Affiliation:

Clc Number:

Fund Project:

  • Article
    • |
  • Figures
    • |
  • Metrics
    • |
  • Reference
    • |
  • Related
    • |
  • Cited by
    • |
  • Materials
    • |
  • Comments
    Abstract:

    Three flexible insulations made from different ceramic fibers were treated at 300益, 600益and 900益
    for 30 min in atmosphere, respectively. Tensile strength was studied with a different variation of the heat treatment
    temperature and fiber surface was observed by SEM. By analyzing the fracture mechanism of the fiber, the main rea鄄
    son leading to the decrease of tensile strength at high temperature was suggested, which was the ablation of agent on
    fiber surface and the crystal transition of amorphous fiber.

    Reference
    Related
    Cited by
Get Citation

Copy
Share
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:
  • Revised:
  • Adopted:
  • Online: November 28,2016
  • Published:

You are the visitor

Beijing Public Network Security：11010602060147号 京ICP备06019415号-2

Address：P.O.Box 9200-73, Beijing 100076, P.R.China

Postcode：100076 Fax：010-68383237

ServiceTel：010-68383269 E-mail：703@china.com

Copyright：Aerospace Materials ＆ Technology ® 2024 All Rights Reserved