Study on the Properties of Flame Retardant Epoxy for Liquid Winding Process
CSTR:
Author:
Affiliation:

1.Aerospace Research Institute of Materials & Processing Technology, Beijing 100076;2.Beijing Aerospace High-tech New Materials Co. Ltd, Beijing 100076

Clc Number:

TB33

  • Article
  • | |
  • Metrics
  • |
  • Reference [15]
  • |
  • Related [20]
  • | | |
  • Comments
    Abstract:

    Aiming at the flame retardant modification of epoxy resin by liquid winding process, the effect of flame retardant addition amount on the properties of resin and composite material was studied. The results show that the viscosity of the resin decreases slightly with the addition of flame retardant, and the curing reactivity does not change significantly. With the increase of flame retardant content, the tensile strength of epoxy resin is basically stable but the impact strength is decreases. The impact strength of epoxy resin added with 30 phr flame retardant is decreased by 44.1% compared with 0 phr. In addition, with the increase of flame retardant content, the thermal decomposition stability of resin is improved, but excessive addition of flame retardant components is not conducive to the stable formation of carbonized layer. According to the above research, the resin system with 20 phr flame retardant additive has the best flame retardant effect, the 50 W vertical combustion test results reach V-0 level, and the mechanical properties have a good retention rate. The tensile strength of NOL ring prepared by modified resin on T700SC reached 2 790 MPa, and the interlayer shear strength is 50.7 MPa. The modified resin and fiber have good interfacial bonding.

    Reference
    [1] 于海宁,高长星,王艳华. 碳纤维增强树脂基复合材料的应用及展望[J]. 合成纤维工业,2020, 43(1): 55-59.YU H N,GAO C X,WANG Y H. Application and prospect of carbon fiber reinforced resin-based composites[J]. China Synthetic Fiber Industry,2020, 43(1): 55-59.
    [2] LIU L,JIA C,HE J,et al.Interfacial characterization, control and modification of carbon fiber reinforced polymer composites[J].Composites Science and Technology,2015, 121: 56-72.
    [3] 崔政粱,刘强,赖丽萍. 碳纤维缠绕复合铝圆管轴向压溃力学性能研究[J].复合材料科学与工程,2020(2): 5-9.CUI Z L,LIU Q,LAI L P.Experimental investigation on the mechanical properties of the CFRP filament winding hybrid tubes under axial crushing[J].Composites Science and Engineering,2020(2): 5-9.
    [4] NEBE M,ASIJEE T J,BRAUN C. Experimental and analytical analysis on the stacking sequence of composite pressure vessels[J]. Compos. Struct.,2020,247: 112429.
    [5] FARD M Y, RAJI B. Hydrostatic and cyclic pressure testing of small-scale composite pipes and vessels[J]. Aerosp. Eng.,2022,35(1): 1-10.
    [6] 张友华,陈连忠,张骞. 导弹发射筒防热材料气动热冲击试验[J]. 宇航材料工艺,2011, 41(2): 128-130.ZHANG Y H,CHEN L Z,ZHANG Q. Aero heating impact experiment on thermal protection materials of missile launch canister[J].Aerospace Materials & Technology. 2011, 41(2): 128-130.
    [7] 魏存磊,徐亚栋,马燕颖. 瞬态冲击载荷下复合材料身管损伤研究[J]. 兵器装备工程学报,2016, 37(7): 131-136.WEI C L ,XU Y D,MA Y Y. Study on damage of composite materials barrel under transient impact load[J]. Journal of Ordnance Equipment Engineering,2016,37(7): 131-136.
    [8] SHI X H, LI X L, LI Y M, et al. Flame-retardant strategy and mechanism of fiber reinforced polymeric composite: A review[J]. Composites Part B-Engineering, 2022, 233:109663.
    [9] WANG D,JIA D.A novel phosphaphenanthrene-based flame retardant for epoxy resins[J]. Polymer International, 2015, 64(5): 648-654.
    [10] SONG P,JIA D,WANG D. Multi-walled carbon nanotubes reinforced epoxy resins with enhanced flame retardancy[J].Polymer International,2016,65(9):1284-1289.
    [11] LIANG B,CAO J,HONG X,et al.Synthesis and properties of a novel phosphorous-containing flame-retardant hardener for epoxy resin[J].Journal of Applied Polymer Science, 2013, 128(5): 2759-2765.
    [12] RAMSDALE-CAPPER R,FOREMAN J P.Internal antiplasticisation in highly crosslinked amine cured multifunctional epoxy resins[J].Polymer,2018, 146: 321-330.
    [13] SCHARTEL B, BALABANOVICH A I, BRAUN U, et al. Pyrolysis of epoxy resins and fire behavior of epoxy resin composites flame-retarded with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide additives[J].Journal of Applied Polymer Science,2007, 104(4): 2260-2269.
    [14] PERRET B, SCHARTEL B, STOSS K, et al. A New halogen-free flame retardant based on 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide for epoxy resins and their carbon fiber composites for the automotive and aviation industries[J].Macromolecular Materials and Engineering,2011,296(1): 14-30.
    [15] ZHANG Q, WANG J, YANG S, et al. Synthesis of a P/N/S-based flame retardant and its flame retardant effect on epoxy resin[J]. Fire Safety Journal,2020, 113(19):102994.
    Cited by
    Comments
    Comments
    分享到微博
    Submit
Get Citation
Share
Article Metrics
  • Abstract:146
  • PDF: 2563
  • HTML: 19
  • Cited by: 0
History
  • Received:January 15,2024
  • Revised:August 20,2024
  • Adopted:May 20,2024
  • Online: September 03,2024
  • Published: August 31,2024
Article QR Code