Analyses on Joint Quality of Spot Welds on SUS304 StainlessSteel Based on Ultrasonic C-Scan

Author:

Affiliation:

Fund Project:

摘要

图/表

访问统计

参考文献

相似文献

引证文献

资源附件

文章评论

摘要:

摇利用超声波水浸聚焦入射法对1 mm 厚的SUS304 奥氏体不锈钢板点焊接头进行超声C 扫描成

像检测;研究了不同焊接工艺参数下获得点焊接头的超声波C 扫描图像特征,据此分析了接头的焊核直径,并

与焊核切口端面尺寸进行了比较;对点焊接头进行了拉伸—剪切试验,测试了接头的力学性能。结果表明:超

声波水浸聚焦入射法能够观测出点焊焊核直径,并能有效地观测出焊核内部形貌特征。当焊接电流为定值(4

kA),供给压力为0. 15 MPa 时,接头出现飞溅、焊穿等缺陷,并且在超声波C 扫描图像中能够清晰地反映出来;

当供给压力为0. 45 MPa 时,虽然点焊焊核直径增大,且未出现焊接缺陷,但是过大的供给压力导致接头厚度变

小,影响了接头抗拉强度。当供给压力为定值(0. 4 MPa),焊接电流为9 kA 时,在C 扫描图像上同样反映出飞

溅、焊穿等典型的焊接缺陷,此时接头的失效载荷及能量吸收值急剧下降。

Abstract:

Abstract摇The quality of spot welds in 1mm SUS304 austenitic stainless steel sheet metal was evaluated by using

ultrasonic water immersion focusing method. The specifics of nugget diameters and the ultrasonic C鄄scan image were

analyzed under different welding process parameters. Furthermore, the tensile鄄shear tests were carried out to examine

the mechanical behavior of sport welds. Results show that the C鄄scan image can get nugget diameter and effective in鄄

formation from the inner pattern of the spot weld based on ultrasonic water immersion focusing method. When the

welding current is 4 kA and the supply pressure is 0. 15 MPa, it can get the information which included splash, solder

to wear and other weld defects from the ultrasonic C鄄scan image. When the supply pressure is 0. 45 MPa, the nugget

diameter is increasing. But the excessive supply pressure leads to the joint thickness decreasing and the joint quality is

failing. When the supply pressure is 0. 4 MPa and the welding current is 9 kA, the failure strength and energy absorp鄄

tion value decrease rapidly, it can get the information which includes splash, solder to wear and other weld defects

from the ultrasonic C鄄scan image

参考文献

相似文献

引证文献

引用本文

张龙曾凯何晓聪邢保英孙鑫宇.基于超声波C 扫描的SUS304 不锈钢板点焊接头质量分析[J].宇航材料工艺,2016,46(2).

复制

文章指标

点击次数:
下载次数:
HTML阅读次数:
引用次数:

历史

收稿日期:
最后修改日期:
录用日期:
在线发布日期: 2016-11-28
出版日期:

期刊介绍

编委会

投稿须知

引用本文

分享

文章指标

历史

文章二维码