铰链接头齿轮断裂失效分析
DOI:
作者:
作者单位:

北京卫星制造厂

作者简介:

通讯作者:

中图分类号:

TG146. 2+1

基金项目:


Fracture Failure Analysis for the Gear of Link Connection
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    某天线系统同步铰链接头在进行展开试验时发生接头齿轮断裂。试验结果表明,其原材料的金
    相组织、化学成分和力学性能均满足标准要求,通过扫描电镜对断齿断口进行微观形貌观察发现,其中一断齿
    的裂纹源区有明显的疲劳条带,其他断齿均为塑性过载断裂形貌,结合天线系统试验过程,判断其失效机理为
    个别轮齿疲劳开裂引起其他齿塑性过载断裂,最终导致整体铰链接头的失效。

    Abstract:

    A gear of an aerial system broke during the unfolding test. A series of test results show that the metallurgical
    structure, the chemical composition, and the mechanical properties of the material all meet the demands of related
    standards. Via scanning electron microscope, the micro appearance of the fracture has been observed. Evident
    fatigue strips were found in the crack characters. Combined with test process of the aerial system, it is concluded that
    the failure mechanism is that the fatigue broken of individual teeth caused the plastic overload fracture of other teeth
    and finally lead to the failure of the whole link connection.

    参考文献
    相似文献
    引证文献
引用本文

孙 璐.铰链接头齿轮断裂失效分析[J].宇航材料工艺,2015,45(1).

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2016-11-28
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭