Modified Shape Memory Epoxy by Blending Polyurethane
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以甲基四氢邻苯二甲酸酐(METHPA) 为固化剂,利用自制的聚氨酯预聚体( PU) 改性环氧树脂
    (TDE-85)制备形状记忆聚合物。研究了形状记忆环氧树脂的力学性能、Tg 和形状记忆性能。研究表明,形状
    记忆环氧树脂的韧性得到明显的提高,Tg 得到了相应的下降,形状记忆性能良好,形状回复率皆在96% 以上,
    形状固定率约达100%。

    Abstract:

    Shape memory epoxy resin of PU/ TDE-85 was prepared by using tetrahydromethyl-1,3-isobenzofurandione(
    METHPA) as a curing agent. The characteristics of the blends were investigated by tensile test, SEM,
    DMA and FTIR. Blends with varying proportions of PU/ TDE-85 were studied for their mechanical properties, thermodynamics,
    glass-transition temperature and shape memory properties. The test results show that the toughness of epoxy
    resin was improved by adding PU. And the glass-transition temperature also decreased accordingly. Moreover, the
    material exhibited a good shape memory performance, the shape recovery and the shape fixity of this material can achieve
    96% and 100%, respectively

    参考文献
    相似文献
    引证文献
引用本文

李芝华.聚氨酯改性环氧树脂形状记忆材料[J].宇航材料工艺,2015,45(1).

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2016-11-28
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭