Curing Characteristics and Adhesive Mechanism WithPMI Foam Core of FM73M Adhesive Film
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用DSC 研究了不同升温速率下FM73M 胶膜的固化反应特性,根据DSC 曲线得到了胶膜的凝
    胶化温度和固化温度等工艺参数,建立了其固化动力学模型,确定胶膜的固化参数为(125±2)℃ /90min。在此
    基础上,通过SEM 研究了胶膜在PMI 泡沫芯材内的分布以及界面结合状况(界面润湿情况、气孔、缺陷),分析
    了胶膜与泡沫芯的胶接机理。

    Abstract:

    The curing characteristics of FM73M adhesive film was monitored by DSC and investigated under different
    heating rates. According to the DSC graph, the theoretical parameters such as gelation temperature, peak temperature
    and the kinetic model of FM73M adhesive film were acquired. And then 125±2℃ /90min is confirmed as the
    actual curing of the film. The distribution of FM73M adhesive film in the PMI foam core and the interface between the
    foam core and the film (interface wetting situation, porosity, defects) were observed by SEM. The adhesive mechanism
    of PMI foam and FM73M adhesive film was analyzed.

    参考文献
    相似文献
    引证文献
引用本文

何 凯. FM73M 胶膜及其与PMI 泡沫芯的胶接机理[J].宇航材料工艺,2013,43(1).

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2016-11-28
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭