The Influence of Different Pressure Difference and Feeding Speed on the Expansion of Carbon Fiber in the Process of Air Flow Spreading
Author:
Affiliation:

1.College of Mechanical Engineering, Tiangong University, Tianjin 300387;2.Key Laboratory of Modern Mechanical and Electrical Equipment Technology, Tianjin 300387

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    为探究气流展纤工艺中不同出口压差和送丝速度对碳纤维丝束展宽效果的影响,依据Venturi原理,搭建气流展纤试验平台,并记录大丝束碳纤维展宽过程,计算不同工艺参数下碳纤维丝束在不同阶段的展宽率和展宽均匀程度。研究结果表明:通过搭建的气流展纤试验台,能获得展宽率高于400%,展宽均匀程度在90%以上的碳纤维丝束,得到的碳纤维丝束的展宽率与出口压差呈正相关,与送丝速度呈负相关;碳纤维丝束的展宽均匀程度与出口压差呈负相关,与送丝速度呈正相关。

    Abstract:

    In order to explore the influence of different outlet pressure difference and feeding speed on the expansion effect of carbon fiber bundles in the air spreading process, an air spreading platform was established according to Venturi principle. The process of carbon fiber broadening was recorded, and the ratio and uniformity of carbon fiber broadening at different stages were calculated under different technological parameters. The results show that the carbon fiber bundles with a broadening rate of more than 400% and a broadening uniformity of more than 90% can be obtained by the air flow spreading test platform.The expansion rate of the carbon fiber bundle is positively correlated with the outlet pressure difference and negatively correlated with the feeding speed. The evenness of the expansion of the carbon fiber bundle is negatively correlated with the outlet pressure difference and positively correlated with the wire feeding speed.

    参考文献
    相似文献
    引证文献
引用本文

牛雪娟,徐妍慧.气流展纤工艺中不同压差和送丝速度对碳纤维展宽的影响[J].宇航材料工艺,2023,53(4):97-102.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2021-08-18
  • 最后修改日期:2021-10-08
  • 录用日期:2021-10-13
  • 在线发布日期: 2023-08-30
  • 出版日期:
第五届航天高分子材料制备与应用工艺技术交流会 征文通知

关闭