一种发射筒用防热涂料的制备与表征
作者:
作者单位:

北京新风航天装备有限公司,北京 100854

作者简介:

通讯作者:

中图分类号:

TQ638

基金项目:


Preparation and Characterization of A Thermal-protection Coating for Launch Canister
Author:
Affiliation:

Beijing Xinfeng Machinery Factory,Beijing 100854

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    为了解决现有发射筒内壁用防热涂料脆性大、附着力差等问题,本文以有机硅改性环氧树脂为基体,添加多种耐高温填料,聚酰胺为固化剂,制备了一种防热涂料,并对其耐焰耐热性能、“三防性”、热老化性能等进行了全面的表征分析。结果表明该涂料能够承受200~300 ℃的长时高温,900 ℃下烧蚀10 s内涂层无变化,且其附着力、“三防性”优良。

    Abstract:

    In order to solve the problems of high brittleness and poor adhesion of the existing thermal-protection coating for the inner wall of launch canister, silicone modified epoxy resin as the matrix, a variety of high-temperature resistant fillers and polyamide as the curing agent were used to prepare the thermal-protection coating. Its flame resistance, heat resistance, "three-proofings" and thermal aging performance had been fully characterized and analyzed. The results show that the coating can withstand a long-term high temperature of 200~300 ℃, ablation at 900 ℃ within 10 s, and its adhesion and "three-proofings" are superior.

    参考文献
    相似文献
    引证文献
引用本文

李盼盼,王猛,刘晓丽,乔懿元,张乐.一种发射筒用防热涂料的制备与表征[J].宇航材料工艺,2023,53(4):70-74.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2021-06-23
  • 最后修改日期:2023-08-19
  • 录用日期:2021-09-28
  • 在线发布日期: 2023-08-30
  • 出版日期: