含硅芳炔树脂改性氰酸酯树脂的性能
作者:
作者单位:

华东理工大学特种功能高分子材料及相关技术教育部重点实验室,上海 200237

作者简介:

袁荞龙,1964年出生,博士,教授,主要从事耐高温树脂的制备改性与应用研究。E-mail:qlyuan@ecust.edu.cn

通讯作者:

中图分类号:

TB35

基金项目:

中央高校基本科研业务费专项资金(222201817001)


Properties of Cyanate Ester Modified by Silicone-containing Arylacetylene Resin
Author:
Affiliation:

Key Laboratory of Specially Functional Polymeric Materials and Related Technology of Ministry of Education,East China University of Science and Technology, Shanghai 200237

Fund Project:

the Fundamental Research Funds for the Central Universities(222201817001)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    将双酚E型氰酸酯(BEDCy)与含硅芳炔树脂(PSA)用溶液共混的方法制备了共混树脂(BEDCy/PSA)。通过DSC和原位红外研究了共混树脂的固化反应,使用TGA和DMA表征了树脂的耐热性能。还考察了共混树脂的介电性能和力学性能。结果表明,PSA树脂能够降低BEDCy树脂的固化温度。随着PSA树脂的添加,氮气和空气氛围下共混树脂固化物的5%热失重温度高于450℃,800℃的残留率分别在80%和19%以上。PSA树脂可以降低BEDCy树脂的介电常数和介电损耗。

    Abstract:

    Bisphenol E cyanate ester (BEDCy) was blended with silicone-containing arylacetylene resin (PSA) to prepare a blended resin (BEDCy/PSA) via solution mixing and evaporation process. The curing reaction of the BEDCy/PSA was studied by DSC and in situ infrared monitoring, the heat resistance of the cured blended resins was characterized by TGA and DMA. The dielectric and mechanical properties of the cured blended resins were further evaluated. The results show that PSA can catalyze the curing reaction of BEDCy. With the addition of PSA resin, the temperature of 5% weight loss and residual yield at 800℃ of the cured blended resins under nitrogen and air atmospheres are higher than 450℃, 80% and 19%, respectively. The dielectric constant and dielectric loss of the cured BEDCy resin decreases upon addition of PSA resin.

    参考文献
    相似文献
    引证文献
引用本文

叶清,袁荞龙,黄发荣.含硅芳炔树脂改性氰酸酯树脂的性能[J].宇航材料工艺,2021,51(2):56-61.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2020-06-18
  • 最后修改日期:2020-09-15
  • 录用日期:2020-09-16
  • 在线发布日期: 2021-05-05
  • 出版日期: 2021-04-25
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭