    由于线胀系数差异大,Cf/SiC复合材料与TC4钛合金钎焊接头容易形成较大的内应力而开裂失效。为了进一步提高接头强度,应用激光毛化工艺在Cf/SiC表面烧蚀出微孔,采用银基钎料对Cf/SiC与TC4进行钎焊。焊后对接头力学性能进行测试,对接头界面及断口显微组织进行观察。结果表明:焊前对Cf/SiC表面进行激光毛化处理,钎料能够填充微孔并形成良好的钎焊界面,能够提高Cf/SiC与TC4钎焊接头的剪切强度。

    Abstract:

    Micro-holes were ablated on the brazing sureface of Cf/SiC CMCs by laser roughing technology. And the Cf/SiC-TC4 brazing joint was achieved by Ag-based filler. Then mechanical properites were tested, the microstructure of the joints and the shear fracture were observed. The results show that, the filler can filled the micro-holes, and the shearing strength of the joints were enhanced.

    参考文献
    相似文献
    引证文献
引用本文

李海刚,毕建勋,马武军,邱金莲,李栋.激光毛化对Cf/SiC与TC4钎焊接头组织及性能的影响[J].宇航材料工艺,2017,47(1):42-46.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-12-05
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2017-02-17
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭