大型飞行器表面烧蚀防热涂层低温快速补涂工艺
作者:
作者单位:

首都航天机械有限公司,北京 100076

作者简介:

通讯作者:

中图分类号:

基金项目:


Low Temperature Rapid Recoating Process of Ablative Insulation Coating for Large Spacecraft
Author:
Affiliation:

Capital Aerospace Machinery Co.,Ltd.Beijing 100076

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用补涂工艺对烧蚀防热涂层进行低温快速补涂,并针对飞行器临飞行前状态,制定了涂层结合力提升、快速固化、多余物控制等的方案。电弧风洞试验表明:补涂涂层烧蚀量小,最高表面温度580 ℃,最高背面温度64 ℃,具有良好的防热性能。采用本工艺补涂涂层进行了多次飞行试验并取得了成功,表明本补涂工艺具有良好的工艺稳定性。

    Abstract:

    The low-temperature rapid recoating process of the ablative anti-heat coating was investigated.Several approaches for improving the adhesion of the coating,rapidly solidifying,and controlling the excess substance were proposed according to the pre-flight state of the aircraft.The wind tunnel test shows that the ablation coating has a small amount of ablation and good heat resistance,with a maximum surface and back temperature of 580 ℃ and 64 ℃,respectively.The coating deposited with this technology is tested successfully in the aerodynamic environment for many times,demonstrating that this recoating process has good process stability.

    参考文献
    相似文献
    引证文献
引用本文

张晶,肖世明,杨立乐,郑玉杰,李庆贺.大型飞行器表面烧蚀防热涂层低温快速补涂工艺[J].宇航材料工艺,2019,49(3):86-90.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-08-03
  • 最后修改日期:2019-05-11
  • 录用日期:2018-10-15
  • 在线发布日期: 2019-06-05
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭