Effect of Pressure Pretreatment on Mechanical Properties of Soft Polyimide Foam
Author:
Affiliation:

Beijing Spacecraft Factory,Beijing 100094

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    为解决软质聚酰亚胺泡沫初始状态力学性能的不稳定性,采用Solimide® AC-550聚酰亚胺泡沫分别进行不同加压方式及加压压力的预压处理,并对预压处理的试样进行拉伸和压缩性能测试。结果表明:负压预处理对该泡沫所造成的力学性能损伤比正压更大;且在+4 kPa预处理时,可使得该泡沫获得相对稳定的力学性能,满足工程应用的需求。

    Abstract:

    In order to solve the mechanical instability of the initial state of soft polyimide foam, the Solimide® AC-550 polyimide foam was used for different pressure and pressure pretreatment respectively, and the tensile and compressive properties of the pretreated samples were tested.The results show that the negative pressure pretreatment damages the mechanical properties caused by the foam,and the pre-treatment at +4 kPa can make the foam obtain relatively stable mechanical properties and meet the needs of engineering applications.

    参考文献
    相似文献
    引证文献
引用本文

崔志刚,张鑫,马立.加压预处理对软质聚酰亚胺泡沫力学性能的影响[J].宇航材料工艺,2019,49(3):51-55.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-07-12
  • 最后修改日期:2019-05-19
  • 录用日期:2018-08-15
  • 在线发布日期: 2019-06-05
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭