Vacuum Brazing Technology of Multi-Brazing Injector
Author:
Affiliation:

Beijing Institute of Control Engineering,Beijing 100190

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    针对不同部位多条钎焊缝一次钎焊成型,开展采用BNi-2钎料进行喷注器真空钎焊工艺方法的实验研究。分析了表面洁净度、钎焊温度及钎缝间隙对喷注器密封性的影响。结果表明:钎缝间隙对由高温合金与不锈钢两种材料组成喷注体钎焊接头的密封性有显著影响。合理的钎缝装配间隙为10~15 μm,此间隙使钎缝中的钎着率>90%,并得到了内外部质量、密封性优良的接头。

    Abstract:

    In order to study the one-shot welding of multiple brazing seams in different parts of the injector,an experimental study on the vacuum brazing process of the injector by using BNi-2 solder was carried out.The effects of surface cleaness, brazing temperature and brazing gap on the sealing performance of the injector were analyzed.The results show that the gaps between brazing seams have an important influence on the sealing performance of the brazed joints of the injection body composed of high temperature alloy and stainless steel.A reasonable brazing seam assembly gap is 10 to 15 μm,and this gap makes the filling rate of the brazing seam more than 90%,and obtains a joint with excellent internal and external quality and sealing property is obtained.

    参考文献
    相似文献
    引证文献
引用本文

王文平,张志伟,武胜勇,贾春林,张汝俊.多钎缝喷注器真空钎焊工艺[J].宇航材料工艺,2019,49(5):92-94.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-03-18
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2019-10-15
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭