Helium Adsorption Capability of High Volume Fraction SiCp/Al composites
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    针对高体分SiCp/Al复合材料气密性问题,系统研究了镀覆、原材料方向性对表面氦气吸附性能影响规律。研究发现该材料经镀覆处理后,其表面氦气吸附合格率提高20%,且随着镀层厚度的增加合格率逐渐提高;不同的机械加工方式对表面氦气吸附合格率影响较小;原材料存在方向各异性,横向切削下料方式下氦气吸附合格率高达91%,纵向切削下料方式下合格率仅为68%。

    Abstract:

    Aiming at the air tightness ofSiCp/Al composites with high volume fraction, the influence of plating and orientation of raw materials on surface helium adsorption properties was systematically studied. It was found that after plating treatment on the high volume fraction of SiCp/Al composite, the qualified rate of the helium adsorption capability increased 20%, and the qualified rate increased gradually with the increase of coating thickness. Difference in mechanical processing has little influence on the qualified rate of the helium adsorption capability. The raw material is anisotropic, the qualified rate of transverse cutting is 91%, and the longitudinal cutting is 68%.

    参考文献
    相似文献
    引证文献
引用本文

刘云彦,李家峰,闻强苗,白晶莹,崔庆新.高体分SiCp/Al复合材料表面吸附氦气特性[J].宇航材料工艺,2018,48(4):85-88.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2017-05-31
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2018-08-18
  • 出版日期:
第十一届航天复合材料成形与加工工艺技术中心交流会 征文通知

关闭